Photomedicine and Laser Surgery Volume 33, Number 2, 2015 ª Mary Ann Liebert, Inc. Pp.1–6 DOI: 10.1089/pho.2014.3818

Effect of Different Temporary Crown Materials and Surface Roughening Methods on the Shear Bond Strengths of Orthodontic Brackets Merve Goymen, DDS, PhD,1 Tolga Topcuoglu, DDS, PhD,2 Sedef Topcuoglu, DDS, PhD,3 and Hakan Akin, DDS, PhD 4

Abstract

Objective: The aim of this study was to evaluate the effect of different temporary crown materials (TCMs) and surface roughening methods on the shear bond strength (SBS) of orthodontic brackets. Background data: TCMs are widely used during orthodontic treatment in teeth in need of prosthetic treatment, to prevent damage to the final restoration. However, there is no consensus considering the best method for roughening of the surface of TCMs. Methods: Five different TCMs [Dentalon Plus-(D), Basworth Trim II-(B), Voco Structure Premium-(V), 3M ESPE Protempt 4-(P), and Revotek LC-(R)] were used in this study. Different surface roughening methods (37% phosphoric acid, sandblasting, and Er:YAG laser) were employed in three subgroups (n = 20). The SBS test was used to assess the durability of all groups. Scanning electron microscopy (SEM) analysis was performed on a representative specimen in each group. Results: The highest mean SBS value was observed in group V, followed by groups D and P, regardless of the surface treatment. The lowest SBS values were observed in group B. The laser-irradiated groups had higher SBS values than the sandblasted and acidetched groups. Furthermore, a significant difference in SBS values was observed between the laser-irradiated group V and all other groups ( p < 0.005). Conclusions: The effects of the chemical nature of TCMs on the SBS values appeared to be clinically negligible, whereas the type of surface treatments had a significant influence on bond strengths. Er:YAG laser irradiation caused a significant increase in bond strength between the TCMs and orthodontic brackets. Interim restorations are used to protect the prepared tooth structure and the pulp from thermal, mechanical, and microbial noxae. They are also required to maintain the existing position of the prepared teeth and gingiva, ensure masticatory function and phonetics, and restore or preserve aesthetic quality until the permanent restoration is inserted.11 Furthermore, TCMs can be used during orthodontic treatment in teeth that require prosthetic treatment to prevent final restoration damages.12 Two major groups of TCMs are available for interim restorations: methacrylate resins and composite-based materials.13 These two major groups can be divided into eight subgroups according to the content material: poly (ethylmethacrylate) (PEMA), poly (methylmethacrylate) (PMMA), epimin resin, bis-acrylic resin, thermoset acrylic resin, urethane dimethacrylate (UDMA)based light-curing resin, cellulose acetate, and polycarbonate (used in prefabricated crowns).14–16

Introduction

B

ecause adult orthodontic treatment has become widespread, the movement of prepared teeth has recently become a basic principle of orthodontic treatment in clinical practice, especially in multidisciplinary cases such as periodontics-orthodontics,1,2 endodontics-orthodontics,3,4 and prosthodontics-orthodontics.5,6 Prosthodontic-orthodontic multidisciplinary approaches are recommended in cases involving hypodontia, polydiastemas, or the lack of edentulous space in which to place a dental implant.7 In such cases, one of the most common problems is the presence of restoratively treated teeth or the necessity for tooth restoration in the mouth. However, the shear bond strength (SBS) values of orthodontic brackets on porcelain, amalgam, and temporary crown materials (TCMs) are less than those on the tooth surface.8–10 1

Department of Orthodontics, Faculty of Dentistry, Gaziantep University, Gaziantep, Turkey. Private orthodontist, Gaziantep, Turkey. Private prosthodontist, Gaziantep, Turkey. 4 Department of Prosthodontics, Faculty of Dentistry, Cumhuriyet University, Sivas, Turkey. 2 3

1

2

GOYMEN ET AL.

Regarding the contents of the crown material, many alternative methods are available for surface preparation prior to orthodontic bonding, such as the diamond bur, sandblasting, acid etching,17 and Er:YAG laser systems18 for the porcelain surface, as well as sandblasting with aluminum oxide particles, the diamond bur, and hydrofluoric acid etching for temporary crowns.19 The wavelength (2.94 lm) of the rays emitted by Er:YAG lasers consisting of Erbium (Er + 3) ions and a yttriumaluminum-garnet (YAG) crystal is very strongly absorbed by water and hydroxyapatite components. This laser system has a wide range of applications in dentistry such as soft tissue surgery,20,21 ablation of hard tissue22 (tooth, bone, and dental calculus), and surface roughening.23–25 Numerous studies have investigated whether the Er:YAG laser is useful for etching dental surfaces. Shiu et al.26 concluded that SBS values were higher in the acid etch and sandblasting groups than in the Er:YAG laser group. However, Kirmali et al.9 showed that Er:YAG laser application increased the SBS values. Similarly, Lee et al.23 reported that Er:YAG laser application can be used as an alternative method to conventional acid etching for roughening the bonding surface. Although many studies assumed that Er:YAG laser irradiation could be used as a new method for roughening various dental surfaces such as enamel and dentin,27,28 amalgam,29 and porcelain,30,31 no studies have evaluated the efficiency of the Er:YAG laser on TCMs. Therefore, the aim of the present study was to evaluate SBS between different types of TCMs and orthodontic brackets, and to investigate the effects of surface roughening methods on the SBS of orthodontic brackets. It was hypothesized that surface modifications would not significantly affect the bond strength between temporary crowns and orthodontic brackets, regardless of the chemical nature or type of TCMs. Materials and Methods

Five different TCMs (Dentalon Plus, Heraeus Kulzer GmbH, Hanau, Germany; Bosworth Trim II, The Harry J. Bosworth Company, Skokie, IL; Structure Premium, Voco GmbH, Cuxhaven, Germany; Protempt 4, 3M ESPE, Neuss, Germany; and Revotek LC, GC, Corp, Tokyo, Japan) were used in the present study. The details regarding the selected

TCMs, such as the manufacturers, compositions, and descriptions, are listed in Table 1. All specimens were prepared in the form of the upper right central incisor. The upper right central incisor was prepared on the model and an impression was taken (Zhermack Zetaplus, Badia Polesine, Italy). The TCMs were made on the plaster models obtained from the impression. Subsequently, the specimens were randomly assigned to three subgroups (n = 20), according to the surface treatments applied. Acid etching: The buccal surfaces of the TCMs were etched with 37% phosphoric acid gel (3M Unitek; Monrovia, CA) for 20 sec, rinsed with a water spray for 15 sec, and dried with a moisture- and oil-free air spray until a dull, frosty appearance was obtained on the crown surface. Sandblasting: The buccal surfaces of the TCMs were sandblasted (Ney, Blastmate II, Yucaipa, CA) with 50 lm Al2O3 particles at four bars of pressure for 3 sec. The specimens were perpendicularly mounted in a special holder in order to maintain a distance of 4 mm between the surface of the specimen and the blasting tip. In addition, the specimens were rinsed under running water and then dried for 10 sec with oil-free compressed air to remove the remnants. Laser irradiation: The buccal surfaces of the specimens were uniformly irradiated for 20 sec with an Er:YAG laser (Light Walker, Fotona, Ljubljana, Slovenia) at power settings of 3 W, 10 Hz, 300 mJ. The beam spot size was 0.63 mm2, the energy density was 47.62 J/cm2, and the power density was 476.2 W/cm2. The laser was applied with sliding on the surface, a noncontact handpiece parallel to the occlusal surface that was positioned 8 mm from the buccal surface of the teeth. One specimen from each different surface treatment modality was used for visual observation of the differences in enamel surfaces by scanning electron microscopy (SEM) ( JSM 6390 LV, Jeol Ltd, Tokyo, Japan) at 1500 · magnification. For all groups, a thin layer of Transbond XT (3M ESPE, USA) light-cured adhesive primer was applied to the crown surface. We used 300 upper right central metal brackets (Master series; American Orthodontics, Sheboygan, WI) in this study. The bracket, with Transbond XT paste on its base, was placed to the center of the middle third of the buccal surface. A sharp scaler was used to remove resin remnants around the brackets. A light-emitting diode (LED)

Table 1. Composition of the Materials Used in the Study Brand name

Description

Main components Poly (ethyl methacrylate)/ poly (methyl acrylate) n-Butyl methacrylate urethanacrylate/ ethylmethacrylate Isobutyl methacrylate di-butyl phthalate dimetyl-p-toluidine Bis-GMA amines benzoyl peroxide butylated hydroxytoluene (BHT) Dimethacrylate polymer Bis-GMA zirconia silica fumed silica silane pigments Urethane dimethacrylate silica crystalline-quartz

Dentalon Plus

D

Powder liquid

Bosworth Trim II

B

Powder liquid

Structur Premium

V

Paste

Protemp 4

P

Paste

Revotek LC

R

Paste

Manufacturer Heraeus Kulzer GmbH, Hanau, Germany The Harry J. Bosworth Company, Skokie, IL Voco GmbH, Cuxhaven, Germany 3M ESPE, Neuss, Germany GC Corp, Tokyo, Japan

BOND STRENGTH OF SOFT DENTURE LINER

3

light cure device (Demi, Kerr Corp, Orange, USA) was used for 20 sec to polymerize the composite beneath the brackets. All teeth were stocked in distilled water at 37C for 24 h and thermocycled (GM, Gokceler Mechanical, Sivas, Turkey) for 500 cycles (5–55C), with a dwell time of 30 sec. A universal testing machine (AGS-X; Shimadzu, Tokyo, Japan) at a constant crosshead speed of 1 mm/min was used to record the SBS of the brackets bonded onto the differentconditioned enamel surfaces, until failure occurred. The buccal surfaces of all teeth embedded in self-curing acrylic were oriented with the testing machine such that tensile force was applied to the bracket in parallel to the long axis of the teeth. The SBS values of all brackets were recorded in megapascals (MPa). SPSS version 11.5 for Windows (SPSS Inc., Chicago, IL) was used for all statistical analyses. One way ANOVA and Tukey’s honest significant difference (HSD) multiple comparison tests were used for independent samples to compare quantitative measurements ( p < 0.05). Results

The mean values and standard deviations of the SBS values for all groups are summarized in Table 2. The highest SBS values were observed in group V, followed by groups D and P, regardless of the surface treatment. The lowest bond strength was observed in group B. The data analysis revealed a significant difference in SBS values between group V and all other groups ( p < 0.05). Furthermore, the laser-irradiated specimens exhibited higher SBS values compared with those of the sandblasting and acid etch specimens. A significant difference in SBS values was found between the laser-irradiated group V and all other groups ( p < 0.005). SEM micrographs of the representative specimens of the investigated pretreatment procedures are presented in Fig. 1A–D. Different degrees of surface roughness were obtained in all groups. The surfaces of acid-etched specimens were flatter than those of the sandblasted specimens. Nevertheless, we found that the morphology of the Er:YAG lasertreated specimens appeared to show a greater increase in roughness than the acid-etched and sandblasted specimens. In all groups, Er:YAG laser-irradiated specimens showed distinctive irregularities.

Discussion

The results obtained in the present study clearly demonstrate that surface treatments with an Er:YAG laser significantly improved the SBS values between the temporary crowns and orthodontic brackets. Although the highest SBS values were observed in group V specimens, which were composite-based materials, group D specimens (methacrylate-based resin) exhibited higher SBS values than those of group R specimens (composite-based resin). Therefore, the null hypothesis, which stated that surface modifications would not significantly affect the bond strength between temporary crowns and orthodontic brackets regardless of the chemical nature or type of TCMs, was rejected. In the literature, limited studies were performed on bond strength between orthodontic bracket and TCM after surface treatments. However, same materials, which were used in the present study, were investigated by the researchers and many studies have reported results that both support and contradict the results of the present study.26,32–41 Gundogdu et al.34 investigated the effects of different surface pretreatments (36% phosphoric acid etching, sandblasting with 50 lm Al2O3 particles, and Er:YAG laser irradiation at 10 Hz 150 mJ) on the bond strength of PMMA denture base material. They reported that sandblasting and Er:YAG laser irradiation are ineffective for improving the bond strength of PMMA resin. Nevertheless, etching with phosphoric acid was found to have improved the bond strength of PMMA resin. Therefore, in the present study, the bonding surface of TCMs was altered with phosphoric acid etching. Al Jabbari et al.35 researched the bond strength between orthodontic brackets and different TCMs after surface modifications, including grinding with silica carbide paper, polishing with pumice, and sandblasting with 50 lm Al2O3 particles. Contrary to the results of the present study, it was presented that sandblasting had a beneficial effect on SBS of the TCMs. Similar results to those of Al Jabbari et al.35 were reported by Blakey and Mah,19 Bahrani and Khaledi,36 and Usumez et al.37 In agreement with the present study, Jacobsen et al.38 and Akin et al.25 exhibited that roughening the PMMA surface by sandblasting with 50 lm Al2O3 particles does not have a positive effect on the bond. Sandblasting with 50 lm Al2O3 particles was used in the present study, because of these conflicting results in the literature.

Table 2. Mean SBS Values with Standard Deviations

Acid etched Sandblasted Laser-irradiated A

Group D

Group B

Group V

Group P

Group R

4.35 – 0.89 4.72 – 1.38A 4.85 – 1.31A,B

2.23 – 0.29 2.74 – 0.55D 4.46 – 0.96A,B,C

5.06 – 1.44A,B,C,F 5.24 – 1.57A,B,C,F,G 6.36 – 1.50

3.68 – 1.22A,B E,F 3.89 – 0.73A,B,C,F,J 5.43 – 0.81A,B,C,F,G,H,I

2.86 – 0.47D,E,J,K 4.06 – 0.48A,B,C,F,G,J,K 4.26 – 0.55A,B,C,F,J,K

Statistical significance between all groups and group D acid etch. Statistical significance between all groups and group D sandblast. Statistical significance between all groups and group D laser. D Statistical significance between all groups and group B acid etch. E Statistical significance between all groups and group B sandblast. F Statistical significance between all groups and group B laser. G Statistical significance between all groups and group V acid etch. H Statistical significance between all groups and group V sandblast. I Statistical significance between all groups and group V laser. J Statistical significance between all groups and group P acid etch. K Statistical significance between all groups and group P sandblast. SBS, shear bond strength. B C

4

GOYMEN ET AL.

FIG 1. Scanning electronic microscopic (SEM) images of group D specimens (original magnification, 1500 · ). (A) Acid etch, (B) Er:YAG laser, (C) sandblast. SEM images of group B specimens (original magnification, 1500 · ). (D) Acid etch, (E) Er:YAG laser, (F) sandblast. SEM images of group V specimens (original magnification, 1500 · ). (G) Acid etch, (H) Er:YAG laser, (I) sandblast. SEM images of group E specimens (original magnification, 1500 · ). ( J) Acid-etch, (K) Er:YAG laser, (L) sandblast. SEM images of group R specimens (original magnification, 1500 · ). (M) Acid-etch, (N) Er:YAG laser, (O) sandblast.

On the other hand, in the literature, there were limited studies about surface modification of PMMA or UDMA resins by using laser irradiation. Laser parameters of 10 Hz, 3W, and 300 mJ were used in the present study because they appeared to be the best parameters for roughening PMMA resins compared with 1W and 100 mJ, 2W and 200 mJ, and 4W and 400 mJ.39 Recently, consistent with the present study, it was demonstrated that altering the PMMA surface by Er:YAG laser significantly increased the bond strengths of PMMA denture base resin.25,39 Conversely, Usumez et al.37 reported that laser treatment of PMMA denture base resin increases the surface roughness and bond strength. However, the increase in bond strength was not statistically significant. Furthermore, it was exhibited that laser irradiation on the bonding surface of UDMA resin effectively increased tensile bond strength between the soft lining material and UDMA resin,40 whereas laser irradiation of the adhesive surface was found

to be ineffective in improving bond strength of denture teeth to UDMA resin.41 Shiu et al.26 reported that the SBS values of the surface roughening method in which only sandblasting was used were higher than those in which sandblasting plus Er:YAG laser irradiation and only a laser were used. On the other hand, in accordance with the results of the present study, Dilber et al.33 showed that roughening with sandblasting plus Er:YAG laser irradiation is more effective than sandblasting. In the present study, the sandblasted and acidetched specimens revealed partially smooth areas in the SEM images when compared with the laser-irradiated specimens. These areas showed reduced surface roughness, which may have been responsible for decreasing the SBS values of the sandblasting and acid applications. Nevertheless, Er:YAG laser application resulted in irregularities and many small pits on the surface of the TCMs. Therefore, adhesive materials can penetrate into the irregularities or

BOND STRENGTH OF SOFT DENTURE LINER

pits produced by the Er:YAG laser and increase the strength of the bond. The main component of both Structure Premium and Protempt 4 is bisphenol A glycerolate dimethacrylate (BisGMA), and many studies have evaluated the SBS of Bis-GMA resin or the effect of its addition to another resin.42,43 In the literature, a consensus has not been reached regarding the effect of Bis-GMA on the SBS. Chen et al.42 reported that the Bis-GMA resin did not significantly affect the bond strength of the zirconia primer, while Kallio et al.43 found that the SBS values of the composite of the Bis-GMA/triethylene glycol dimethacrylate (TEGDMA) substrate were significantly higher than those of other substrates. According to the results of the present study, the addition of Bis-GMA resin increased the bond strength of orthodontic brackets. Rambhia et al.10 demonstrated that the SBS values of orthodontic brackets to TCMs ranged from 2.81 to 9.65 MPa. Further, these authors found that the SBS of Protemp ranged from 8.33 to 9.65 MPa, which is significantly higher than the results of the present study (3.68 MPa). The bonded specimens were stored in distilled water for 24 h prior to the SBS test in the study by Rambhia et al.,10 whereas the bonded specimens were maintained in a thermocycling machine for 500 cycles in the present study. This likely explains why the values in the present study were lower than those of Rambhia et al. On the other hand, according to literature, several studies reported that the SBS value must be at least 5 MPa,44 whereas others suggested that it should range from 6.5 to 10 MPa.45 In the present study, the SBS value of group V was > 5 MPa, regardless of the surface treatment. In addition, the laser-irradiated specimens of group P exhibited SBS values that were > 5 MPa. Others were not presented sufficient SBS values to withstanding orthodontic force. Conclusions

Within the limitations of this study, it was concluded that the type of surface treatment, especially Er:YAG laser irradiation, has a significant influence on the bond strength between TCMs and orthodontic brackets. Furthermore, all group V specimens and only laser-irradiated group P specimens presented SBS values > 5 MPa, which is a clinically acceptable value. Author Disclosure Statement

No competing financial interests exist. References

1. Ong MA, Wang HL, Smith FN. Interrelationship between periodontics and adult orthodontics. J Clin Periodontol 1998;25:271–277. 2. Pontoriero R, Celenza Jr F, Ricci G, Carnevale G. Rapid extrusion with fiber resection: a combined orthodonticperiodontic treatment modality. Int J Periodont Rest 1987; 7:30. 3. Heithersay GS. Combined endodontic-orthodontic treatment of transverse root fractures in the region of the alveolar crest. Oral Surg Oral Med Oral Pathol 1973;36: 404–415. 4. Simon JH, Lythgoe JB, Torabinejad M. Clinical and histologic evaluation of extruded endodontically treated teeth in dogs. Oral Surg Oral Med Oral Pathol 1980;50:361–371.

5

5. Shiloah J. Clinical crown lengthening by vertical root movement. J Prosthet Dent 1981;45:602–605. 6. Johnson GK, Sivers JE. Forced eruption in crown-lengthening procedures. J Prosthet Dent 1986;56:424–427. 7. Planning OT. Congenitally missing maxillary lateral incisors and orthodontic treatment considerations for the single-tooth implant. J Can Dent Assoc 2001;67: 25–28. 8. Stangel I, Nathanson D, Hsu C. Shear strength of the composite bond to etched porcelain. J Dent Res 1987;66:1460– 1465. 9. Kirmali O, Akin H, Ozdemir AK. Shear bond strength of veneering ceramic to zirconia core after different surface treatments. Photomed Laser Surg 2013;31:261–268. 10. Rambhia S, Heshmati R, Dhuru V, Iacopino A. Shear bond strength of orthodontic brackets bonded to provisional crown materials utilizing two different adhesives. Angle Orthod 2009;79:784–789. 11. Balkenhol M, Meyer M, Michel K, Ferger P, Wo¨stmann B. Effect of surface condition and storage time on the repairability of temporary crown and fixed partial denture materials. J Dent 2008;36:861–872. 12. Kokich VG, Spear FM. Guidelines for managing the orthodontic-restorative patient. Semin Orthod 1997;3:3–20. 13. Balkenhol M, Ferger P, Mautner MC, Wo¨stmann B. Provisional crown and fixed partial denture materials: mechanical properties and degree of conversion. Dent Mater 2007;23:1574–1583. 14. Vahidi F. The provisional restorations Dent Clin North Am 1987;31:363–381. 15. Larson WR, Dixon DL, Aquilino SA, Clancy JM. The effect of carbon graphite fiber reinforcement on the strength of provisional crown and fixed partial denture resins. J Prosthet Dent 1991;66:816–820. 16. Anderson JN. Applied Dental Materials. 7th ed. Oxford: Blackwell Scientific Publications, 1990. 17. Kussano CM, Bonfante G, Batista JG, Pinto J. Evaluation of shear bond strength of composite to procelain according to surface treatment. Braz Dent J 2003;14:132–135. 18. Akova T, Yoldas O, Toroglu MS, Uysal H. Porcelain surface treatment by laser for bracket-porcelain bonding. Am J Orthod Dentofacial Orthop 2005;128:630–637. 19. Blakey R, Mah J. Effects of surface conditioning on the shear bond strength of orthodontic brackets bonded to temporary polycarbonate crowns. Am J Orthod Dentofacial Orthop 2010;138:72–78. 20. Watanabe H, Ishikawa I, Suzuki M, Hasegawa K. Clinical assessments of the erbium:YAG laser for soft tissue surgery and scaling. J Clin Laser Med Surg 1996;14:67–75. 21. Fornaini C. Er: YAG and adhesion in conservative dentistry: clinical overview. Laser Ther 2013;22:31. 22. Schwarz F, Sculean A, Georg T, Reich E. Periodontal treatment with an Er: YAG laser compared to scaling and root planning: a controlled clinical study. J Periodontol 2001;72:361–367. 23. Lee BS, Hsieh TT, Lee YL, et al. Bond strengths of orthodontic bracket after acid-etched, Er: YAG laserirradiated and combined treatment on enamel surface. Angle Orthod 2003;73:565–570. 24. Topcuoglu T, Oksayan R, Ademci KE, Goymen M, Usumez S, Usumez A. Effects of water flow rate on shear bond strength of orthodontic bracket bonded to enamel surface after Er:YAG laser ablation. Photomed Laser Surg 2013;31:486–491.

6

25. Akin H, Tugut F, Mutaf B, Akin G, Ozdemir AK. Effect of different surface treatments on tensile bond strength of silicone-based soft denture liner. Lasers Med Sci 2011;26:783–788. 26. Shiu P, De Souza–Zaroni WC, Eduardo CP, Youssef MN. Effect of feldspathic ceramic surface treatments on bond strength to resin cement. Photomed Laser Surg 2007;25: 291–296. 27. Hossain M, Nakamura Y, Yamada Y, Suzuki N, Murakami Y, Matsumoto K. Analysis of surface roughness of enamel and dentin after Er, Cr: YSGG laser irradiation. J Clin Laser Med Surg 2001;19:297–303. 28. Usumez A, Aykent F. Bond strengths of porcelain laminate veneers to tooth surfaces prepared with acid and Er, Cr: YSGG laser etching. J Prosthet Dent 2003;90:24–30. 29. Oskoee PA, Kachoei M, Rikhtegaran S, Fathalizadeh F, Navimipour EJ. Effect of surface treatment with sandblasting and Er, Cr: YSGG laser on bonding of stainless steel orthodontic brackets to silver amalgam. Med Oral Patol Oral Cir Bucal 2012;17:e292. 30. Topcuoglu T, Oksayan R, Topcuoglu S, Coskun ME, Isman NE. Effect of Er: YAG laser pulse duration on shear bond strength of metal brackets bonded to a porcelain surface. Photomed Laser Surg 2013;31:240–246. 31. Akin H, Tugut F, Akin GE, Guney U, Mutaf B. Effect of Er: YAG laser application on the shear bond strength and microleakage between resin cements and Y-TZP ceramics. Lasers Med Sci 2012;27:333–338. 32. Rodriguez–Vilchis LE, Contreras–Bulnes R, Olea–Mejia OF, Sanchez–Flores I, Centeno–Pedraza C. Morphological and structural changes on human dental enamel after Er:YAG laser irradiation: AFM, SEM, and EDS evaluation. Photomed Laser Surg 2011;29:493–500. 33. Dilber E, Yavuz T, Kara HB, Ozturk AN. Comparison of the effects of surface treatments on roughness of two ceramic systems. Photomed Laser Surg 2012;30:308–314. 34. Gundogdu M, Yesil Duymus Z, Alkurt M. Effect of surface treatments on the bond strength of soft denture lining materials to an acrylic resin denture base. J Prosthet Dent 2014;112:964–971. 35. Al Jabbari YS, Al Taweel SM, Al Rifaiy M, Alqahtani MQ, Koutsoukis T, Zinelis S. Effects of surface treatment and artificial aging on the shear bond strength of orthodontic brackets bonded to four different provisional restorations. Angle Orthod 2014;84:649–555.

GOYMEN ET AL.

36. Bahrani F, Khaledi AA. Effect of surface treatments on shear bond strength of denture teeth to denture base resins. Dent Res J (Isfahan) 2014;11:114–118. 37. Usumez A, Inan O, Aykent F. Bond strength of a silicone lining material to alumina-abraded and lased denture resin. J Biomed Mater Res Part B: Appl Biomater 2004;71:196–200. 38. Jacobsen NL, Mitchell DL, Johnson DL, Holt RA. Lased and sandblasted denture base surface preparations affecting resilient liner bonding. J Prosthet Dent 1997;78:153–158. 39. Tugut F, Akin H, Mutaf B, Akin G, Ozdemir AK. Strength of the bond between a silicone lining material and denture resin after Er:YAG laser treatments with different pulse durations and levels of energy. Lasers Med Sci 2012;27: 281–285. 40. Akin H, Tugut F, Guney U, Kirmali O, Akar T. Tensile bond strength of silicone-based soft denture liner to two chemically different denture base resins after various surface treatments. Lasers Med Sci 2013;28:119–123. 41. Akin H, Tugut F, Guney U, Akar T. Shear bond strength of denture teeth to two chemically different denture base resins after various surface treatments. J Prosthodont 2014; 23:152–156. 42. Chen L, Shen H, Suh BI. Effect of incorporating BisGMA resin on the bonding properties of silane and zirconia primers. J Prosthet Dent 2013;110:402–407. 43. Kallio T, Lastumaki T, Vallittu P. Effect of resin application time on bond strength of polymer substrate repaired with particulate filler composite. J Mater Sci Mater Med 2013;14:999–1004. 44. Elekdag–Turk S, Sarac YS, Turk T, Sarac D. The effect of a light-emitting diode on shear bond strength of ceramic brackets bonded to feldspathic porcelain with different curing times. Eur J Orthod 2007;29:299–303. 45. Lopez JL. Retentive shear strengths of various bonding attachment bases. Am J Orthod 1980;77:669–678.

Address correspondence to: Merve Goymen Department of Orthodontics The Faculty of Dentistry Gaziantep University 27310, Gaziantep Turkey E-mail: [email protected]

Effect of different temporary crown materials and surface roughening methods on the shear bond strengths of orthodontic brackets.

The aim of this study was to evaluate the effect of different temporary crown materials (TCMs) and surface roughening methods on the shear bond streng...